321 Stainless Steel Plate Description
321 stainless steel has better crack resistance during the welding process due to the titanium content. In addition, 321 stainless steel also has good processing and welding properties, making it easy to perform cutting, bending, welding and other processing operations. Its mechanical properties such as tensile strength, flexural strength and elongation are also excellent, and can meet the requirements of use in various complex environments. Because 321 stainless steel have excellent corrosion resistance and high temperature performance, they are widely used in petroleum, chemical industry, aviation, aerospace and other fields. In the petroleum and chemical industries, since the production process involves a large amount of corrosive media such as acids, alkalis, and salts, 321 stainless steel can effectively resist the corrosion of these media and ensure the long-term stable operation of the equipment. In the aviation and aerospace fields, 321 stainless steel has become one of the important structural materials due to high operating temperatures and the requirement for materials with good creep resistance.
Product Parameters
| Product Name | 321 Stainless Steel Plate |
| Type | Plate |
| Thickness | 0.3mm-200mm |
| Length | 2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. |
| Width | 40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
| Surface | BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
| Scope of Application | Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging,
Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. |
| Certificate | ISO, SGS, BV, etc. |
| Production Technology | Hot Rolling, Cold Rolling |
| Edge Processing | Edging, Trimming |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
| ≤ 0.08 | ≤ 0.75 | ≤ 2.0 | 17.0～19.0 | 9.0～12.0 | ≤ 0.03 | ≤ 0.045 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥520 | ≥205 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
| 7.92 | 193 | 16.6 | 16.0 | 72 |
Surface Selection